Pulsed Direct liquid Injection ALD of TiO2 Films Using Titanium Tetraisopropoxide Precursor
2013
Abstract TiO 2 thin films are grown by pulsed direct liquid injection atomic layer deposition with rapid thermal heating using titanium tetraisopropoxide and water vapor as precursors. The ALD growth rate is constant in the saturation zone range 35-47 ms at the temperature deposition of 280 °C. The TiO 2 growth rate of 0.018 nm/cycle was achieved in a self-limited ALD mode. SEM and AFM analysis showed the as-deposited films have a smooth surface with a low roughness. XPS analysis exhibited the stoichiometry of TiO 2 in the homogenous depth composition.
Microstructural and tribological study of Nd:YAG laser treated titanium plates.
2008
Abstract In this work, the fretting behaviour of pure Ti plates laser treated with a Nd:YAG pulsed laser was compared to that of untreated Ti plates. Fretting tests were done at room temperature without lubrication. The contact geometry was a cylinder (bearing steel) on a plane. The evolution of both the ratio, μ = Q / P , between the normal and the tangential forces, and the Fouvry's energy criterion ( A ) were recorded as a function of the number of fretting cycles, N . Energy dispersive spectrometry and micro-Raman spectroscopy were used to analyse the fretting scars. The oxidized layer formed by the laser treatment displayed a mixed slip regime as a function of N , and a smaller frettin…
Development of the microwave transduction applied to ammonia detection : from nanomaterials to broadband sensor, understanding of the mechanisms and …
2017
The main objective of this thesis is to propose an analysis of the microwave transduction specificities in the framework of ammonia sensing applications. The two main features of this transduction are its broadband characterization (1 to 8 GHz) as well as its sensitive materials (dielectrics). This transduction method is based on the interaction between a polluting gas and a sensitive material deposited on the surface of a microwave-specific propagating structure. The response of the sensor is not directly induced by the dielectric properties of the gaseous target molecule, but rather by those of the target species adsorbed on the surface of the sensitive material. This adsorption causes a …